This cutting method uses a gas and oxygen flame to heat the steel to a flammable point, and then burn it in an oxygen cutting stream. This process is only performed in a very narrow area (<1mm), and the adjacent cutting edge is heated to the hardening temperature (austenitizing). Due to the very high heat flow flowing into the surrounding cold material, it transforms into a hardened structure.
This kind of heat diffusion in water can reach the cooling rate of quenching, and the surrounding area is tempered, which we call the heat affected zone (HAZ). The large temperature difference causes stress and hardening cracking. With the increase of thickness and alloy content,
wear-resistant steel requires more caution than ordinary steel when flame cutting.
AHL STEEL specializes in sales of wear-resistant steel plates and processing of wear-resistant parts, providing customers with high-quality one-stop services. There are more than 2,000 tons of imported and domestic wear-resistant plates in stock. With many years of experience, we can quickly and accurately perform
NM400 wear-resistant plates, WearTuf450 cutting, Hardox500 machining, drilling, bending, rounding, welding, stud welding and other processing.
The wear resistant steel and corten steel products provided by AHL STEEL are well received by customers. Welcome everyone to come to purchase and consult.
Email: Info@AHL Steel .com